Product Description
A1 A2 3D 1050MPA Dental Zirconia Block For Laboratorio Dental



A1 A2 3D Pro Multilayer Zirconia Block Blank Disc for Laboratorio Dental, 43% to 57% 1050MPA 3D Pro Multi Layer Zircon



Dental Consumables 3D Pro Multilayer Zirconia Block Disc Disks With 16 Shades For Open CADCAM System In Laboratorio Dental



Detailed Product Description of 3D Plus Multilayer Zirconia Block:

Name Yucera 3D plus multilayer zirconia block
Sintered Density 6.07 ± 0.03g/cm3
Hardness 1200HV
Sintering Temperature Recommend 1500℃
Bending Strength 1050Mpa-700Mpa
Translucency 43%-57%



Yucera 3D plus multilayer zirconia block is the most high end class zirconia, the most nature zirconia, which changes color(from dark to light) , strength( from 1050mpa-700mpa), and translucency(43%-57%) gradually from cervical to incisal part at one multilayer zirconia block.

This multilayer zirconia block can make both posterior teeth and anterior teeth. One zirconia to cover all indications.



Some customer feedback to us that they prefer our 3D plus multilayer more than Aidite 3D pro and Ivoclar zircad Prime.



Application/Indication of Yucerta 3D plus multilayer zirconia block:



Veneer



Posterior crown



Full crown bridge



Anterior crown



InlayFull contour screw retained bridge



Full arch crown bridge



Implant



Available shades and sizes of Yucera 3D plus multilayer zirconia block:

Open System Zironzahn System Amann Girrback Available Shades
98*10mm 95*10mm 89*71*10mm A1-D4, BL1, BL2, BL3
98*12mm 95*12mm 89*71*12mm A1-D4, BL1, BL2, BL3
98*14mm 95*14mm 89*71*14mm A1-D4, BL1, BL2, BL3
98*16mm 95*16mm 89*71*16mm A1-D4, BL1, BL2, BL3
98*18mm 95*18mm 89*71*18mm A1-D4, BL1, BL2, BL3
98*20mm 95*20mm 89*71*20mm A1-D4, BL1, BL2, BL3
98*22mm 95*22mm 89*71*22mm A1-D4, BL1, BL2, BL3
98*25mm 95*25mm 89*71*25mm A1-D4, BL1, BL2, BL3


Features of Yucera 3D plus multilayer zirconia block:

1. Sintered Density of multilayer zirconia block: 6.07 ± 0.03g/cm3

2. Outstanding aesthetics – highly esthetic, monolithic single-tooth and bridge restorations in the anterior and posterior region.

3. Translucency of multilayer zirconia block 57-43%, adjusted translucency gradient ensures good coverage in the cervical area and increased translucency in the incisal area.

4. The integrated color gradient also ensures the efficient fabrication of natural-looking restorations.

5. Extensive color selection – 19 colors (Blench, A1-D4).

6. Bending Strength of multilayer zirconia blank :700-1050 MPa

7. Hardness of multilayer zirconia block 1200HV

8. Wide range of indications – from single-tooth restoration to multi-unit bridge.

9. Self-colored dental multilayer zirconia block

10. CAD CAM digital system



Sintering step for dental 3D pro multilayer zirconia block:



Sintering step Start Temperature(℃) End Temperature(℃) Time(Min) Rate(℃/Min)
Step 1 20 900 90 9.7
Step 2 900 900 30 0
Step 3 900 1500 180 3.3
Step 4 1500 1500 120 0
Step 5 1500 800 60 -11.6
Step 6 800 natural cooling 20 120 -6.5


Yucera's dental 3D pro multilayer zirconia block, real case:

A1 A2 3D 1050MPA Dental Zirconia Block For Laboratorio Dental 0A1 A2 3D 1050MPA Dental Zirconia Block For Laboratorio Dental 1