PU Foam Materials Wannate Pm 200 TDI MDI Polyurethane
1. Applications WANNATE® PM-200 is a diisocyanate-diphenylmethane (MDI)-based composition containing some higher functionality isocyanates. It is a brown liquid at ambient temperatures. WANNATE® PM-200 can be widely used in the production of rigid PU foam heat-insulating materials; also used in ...
1. Applications
WANNATE® PM-200 is a diisocyanate-diphenylmethane (MDI)-based composition containing some higher functionality isocyanates. It is a brown liquid at ambient temperatures. WANNATE® PM-200 can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam, cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, WANNATE® PM-200 can provide better flow ability. It is, therefore, particularly suitable for the production which require strict flow ability of systems.
2. Typical Physical and Chemical Properties
Test Item(s) Specifications
Appearance Brown Liquid
Viscosity(25℃)/(mPa·s) 150-250
NCO Content/% 30.5-32.0
Density (25℃)/(g/cm3 ) 1.220-1.250
Acid Content/% ≤0.030
Hydrolysable Chlorine/% ≤0.20
3. Package(s)
210L iron drums, 250kg/drum
4. Storage
Since WANNATE® PM-200 is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product. Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen. Containers of WANNATE® PM-200 should be kept properly closed and stored indoors at ambient temperature (15-35℃) in a well-ventilated area. Storage at low temperature (below 5℃) may lead to some crystallization; this material must, therefore, be protected from frost. PM-200 2 / 2 Wanhua Chemical Group Co., LTD If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80℃ to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended. Extended storage at temperatures above 50℃ is not recommended to prevent from the formation of insoluble solids and viscosity increase.
5. Shelf Life
Under recommended storage conditions, the shelf life of WANNATE® PM-200 is one year since the date of production.
WANNATE® PM-200 is a diisocyanate-diphenylmethane (MDI)-based composition containing some higher functionality isocyanates. It is a brown liquid at ambient temperatures. WANNATE® PM-200 can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam, cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, WANNATE® PM-200 can provide better flow ability. It is, therefore, particularly suitable for the production which require strict flow ability of systems.
2. Typical Physical and Chemical Properties
Test Item(s) Specifications
Appearance Brown Liquid
Viscosity(25℃)/(mPa·s) 150-250
NCO Content/% 30.5-32.0
Density (25℃)/(g/cm3 ) 1.220-1.250
Acid Content/% ≤0.030
Hydrolysable Chlorine/% ≤0.20
3. Package(s)
210L iron drums, 250kg/drum
4. Storage
Since WANNATE® PM-200 is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product. Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen. Containers of WANNATE® PM-200 should be kept properly closed and stored indoors at ambient temperature (15-35℃) in a well-ventilated area. Storage at low temperature (below 5℃) may lead to some crystallization; this material must, therefore, be protected from frost. PM-200 2 / 2 Wanhua Chemical Group Co., LTD If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80℃ to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended. Extended storage at temperatures above 50℃ is not recommended to prevent from the formation of insoluble solids and viscosity increase.
5. Shelf Life
Under recommended storage conditions, the shelf life of WANNATE® PM-200 is one year since the date of production.